Influence of disodium (1-hydroxythylidene) diphosphonate on bonding between glass-ceramics containing apatite and wollastonite and mature male rabbit bone

  • Laboratory Investigations
  • Published:
Calcified Tissue International Aims and scope Submit manuscript

Summary

It has been reported that bioactive glass-ceramics containing crystalline oxy- and fluoroapatite [Ca10(PO4)6(O,F2) and wollastonite (CaSiO3), chemical composition: MgO 4.6, CaO 44.9, SiO2 34.2, P2O5 16.3, CaF2 0.5 in weight ratio] bond to bone tissue through the formation of an apatite (a calcium and phosphorus-rich layer) on the ceramic surface. In this study, the influence of disodium (1-hydroxythylidene) diphosphonate (DHTD) on the bonding between bone and glass-ceramics containing apatite and wollastonite was investigated. Rectangular ceramic plates (15 mm x 10 mm x 2 mm, abraded with #2000 alumina powder) were implanted into the tibial bone of mature male rabbits. DHTD was administered daily by subcutaneous injection to groups 1–5: group 1–4 at doses of 20, 5.0, 1.0, and 0.1 mg/kg body wt/day for 8 weeks; and group 5 at a dose of 5 mg/kg body wt/day for 4 weeks. Group 6 was given injections of saline as a control. At 8 weeks after implantation, the rabbits were killed. The tibiae containing the ceramics were dissected out and used for a detachment test. The failure load, when an implant became detached from the bone, or when the bone itself broke, was measured. The failure loads for groups 1–6 were 0 kg, 0 kg, 8.08±2.43 kg, 7.28±2.07 kg, 5.56±1.63 kg, and 6.38±1.30 kg, respectively. Ceramic bonding to bone tissue was inhibited by a higher dose of DHTD (groups 1 and 2). In groups 3–6, SEM-EPMA showed a calcium-phosphorus-rich layer (Ca-P-rich layer) at the interface between the ceramic and bone tissue. However, at higher doses (5 and 20 mg), the Ca-P-rich layer was not observed on the surface of the glass-ceramic. DHTD suppressed both the formation of the Ca-P-rich layer on the surface of galss-ceramics and also apatite formation by bone. Thus, bonding between the Ca-P-rich layer of glass-ceramics and the apatite of bone tissue did not occur. This study verified that the apatite crystals in bone tissue bonded chemically to the Ca-P-rich layer on the surface glass-ceramics. The organic matrix (osteoid) did not participate in the bonding between bone and glass-ceramics.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Kokubo T, Shigematsu M, Nagashima Y, Tashiro M, Nakamura T, Yamamuro T, and Higashi S (1982) Apatite- and wollastonite-containing glass-ceramic for prosthetic application. Bull Inst Chem Res, Kyoto Univ, 60:260–268

    Google Scholar 

  2. Nakamura T, Yamamuro T, Higashi S, Kokubo T, Itoo S (1985) A new glass-ceramic for bone replacement: evaluation of its bonding ability to bone tissue. J Biomed Mater Res 19:685–698

    Google Scholar 

  3. Kitsugi T, Yamamuro T, Nakamura T, Higashi S, Kakutani Y, Hyakuna K, Ito S, Kokuko T, Takagi M, Shibuya T (1986) Bone bonding behavior of three kinds of apatite-containing glassceramics. J Biomed Mater Res 20:1295–1307

    Google Scholar 

  4. Kitsugi T, Yamamuro T, Nakamura T, Kokubo T, Shibuya T, Takagi M (1987) SEM-EPMA observation of three types of apatite-containing glass-ceramics implanted in bone: the variance of a Ca-P rich layer. J Biomed Mater Res 21:1255–1271

    Google Scholar 

  5. Kokubo T, Kushitani H, Sakka S, Kitsugi T, Yamamuro T (1990) Solutions able to reproduce in vivo surface-structure changes in bioactive glass-ceramic A-W3. J Biomed Mater Res 24:721–734

    Google Scholar 

  6. Kokubo T, Ito S, Huang ZT, Hayashi T, Sakka S, Kitsugi T, Yamamuro T (1990) Ca, P-rich layer formed on high-strength bioactive glass-ceramic A-W. J Biomed Mater Res 24:331–343

    Google Scholar 

  7. Kokubo T (1990) Surface chemistry of bioactive glass-ceramics. J Noncrystalline Solids 120:138–151

    Google Scholar 

  8. Yamamuro T, Nakamura T, Higashi S, Kasai R, Kakutani Y, Kitsugi T, Kokubo T (1984) an artificial bone for use as a bone prosthesis. In Atumi K, Maekawa M, Ota K (eds) Progress in artificial organs-1983, vol. 2. ISAO Press No. 204, Cleveland, pp 810–814

  9. Yamamuro T, Shikata T, Okumura H, Kitsugi T, Kakutani Y, Matsui T, Kokubo T (1990) Replacement of the lumbar vertebrae of sheep with ceramic prostheses. J Bone Joint Surg 72-B: 889–893

    Google Scholar 

  10. Rosenblum IY (1974) The effects of disodium ethane-1-hydroxy-1,1-diphosphonate (EHDP) on bone and serum chemistry in rabbits. Calcif Tissue Res 16:145–152

    Google Scholar 

  11. Plasmans CMT, Kuypers W, Slooff TJJ (1978) The effect of ethane-1-hydroxy-1, 1-diphosphonic acid (EHDP) on matrix-induced ectopic bone formation. Clin Orthop Rel Res 132:233–243

    Google Scholar 

  12. Schenk R, Merz WA, Mühlbauer R, Russell RGG, Fleisch H (1973) Effect of ethane-1-hydroxy-1,1-diphosphonate (EHDP) and dichloromethylene diphosphonate (Cl2MDP) on the calcification and resorption of cartilage and bone in the tibial epiphysis and metaphysis of rats. Calcif Tissue Res 11:196–214

    Google Scholar 

  13. Kokubo T, Ito S, Sakka S, Yamamuro T (1985) Mechanical properties of a new type of apatite-containing glass-ceramic for prosthetic application. J Mat Sci 20:2001–2004

    Google Scholar 

  14. Gross UM, Strunz V (1977) Surface staining of sawed sections of undecalcified bone containing alloplastic implant. Stain Technol 52:217–219

    Google Scholar 

  15. Russell RGG, Kislig A-M, Casey PA, Fleisch H, Thornton J, Schenk R, Williams DA (1973) Effects of diphosphonates and calcitonin on the chemistry and quantitative histology of rat bone. Calcif Tissue Res 11:179–195

    Google Scholar 

  16. Russell RGG, Fleisch H (1975) Pyrophosphate and diphosphonates in skeletal metabolism. Physiological, clinical, and therapeutic aspects. Clin Orthop Rel Res 108:241–263

    Google Scholar 

  17. Thomas BJ, Amstutz HC (1985) Results of the administration of diphosphonate for theprevention of heterotopic ossification after total hip arthroplasty. J Bone Joint Surg 67-A:400–403

    Google Scholar 

  18. King WR, Francis MD, Michael WR (1971) Effect of disodium ethane-1-hydroxy-1,1-diphosphonate on bone formation. Clin Orthop Rel Res 78:251–270

    Google Scholar 

  19. Graham R, Russell G, Smith R (1973) Diphosphonates. Experimental and clinical aspects. J Bone Joint Surg 55B:66–86

    Google Scholar 

  20. Kitsugi T, Yamamuro T, Nakamura T, Kokubo T, Takagi M, Shibuya T, Takeuchi H, Ono M (1987) Bonding behavior between two bioactive ceramics in vivo. J Biomed Mater Res 21:1109–1123

    Google Scholar 

  21. Kitsugi T, Yamamuro T, Kokubo T (1990) Analysis of AW glass-ceramic surface by micro-beam x-ray diffraction. J Biomed Mater Res 24:259–273

    Google Scholar 

  22. Neo M, Kotani S, Fujita Y, Nakamura T, Tamamuro T, Bando Y, Ohtsuki C, Kokubo T (1992) Differences in ceramic-bone interface between surface-active ceramics and resorbable ceramics; a study by scanning and transmission electron microscopy. J Biomed Mater Res 26:255–267

    Google Scholar 

  23. Kitsugi T, Yamamuro T, Neo M, Nakamura T, Oka M, Kokubo T (1992) Influence of EHDP on bonding between calcium phosphate ceramics and mature male rabbit bone. J Jpn Orthop Asson 66:S-1119 (in Japanese)

    Google Scholar 

  24. Nilles JL, Coletti JM, Wilson C (1973) Biomechanical evaluation of bone-porous material interface. J Biomed Mater Res 7:231–252

    Google Scholar 

  25. Colella SM, Miller AG, Stang RG, Stoebe TG, Spengler DM (1981) Fixation of porous titanium implants in cortical bone enhanced by electrical stimulation. J Biomed Mater Res 15:37–46

    Google Scholar 

  26. Miller GT, Greenspan DC, Piotrowski G, Hench LL (1977) Mechanical evaluation of bone-bioglass bonding, in an investigation of bonding mechanisms of the interface of a prosthetic material. U.S. Army Medical Research and Development Command, Contract No DAMD 17-76-C-6033, Report No. 7:24–39

  27. Kitsugi T, Yamamuro T, Kokubo T (1989) Bonding behavior of a glass-ceramic-containing apatite and wollastonite in segmental replacement of the rabbit tibia under load-bearing conditions. J Bone Joint Surg 71-A:264–272

    Google Scholar 

  28. Fleisch H, Russell RGG, Francis MD (1969) Diphosphonates inhibit hydroxyapatite dissolution in vitro and bone resorption in tissue culture in vivo. Science 165:1262–1264

    Google Scholar 

  29. Michael MR, King WR, Francis MD (1971) Effectiveness of diphosphonates in preventing “osteoporosis” of disuse in the rat. Clin Orthop Rel Res 78:271–276

    Google Scholar 

  30. Bijvoet OLM, Nollen AJG, Slooff TJJH, Feith R (1974) Effect of a diphosphonate on para-articular ossification after total hip replacement. Act Orthop Scand 45:926–934

    Google Scholar 

  31. Nollen AdJG (1986) Effects of ethylhydroxydiphosphonate (EHDP) on heterotopic ossification. Acta Orthop Scand 57:358–361

    Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Orthopaedic Surgery, Faculty of Medicine, Kyoto University, 54 Kawaharacho Shogoin, Sakyo-ku, 606, Kyoto, Japan

    Toshiaki Kitsugi & Takao Yamamuro

  2. Research Center for Biomedical Engineering, Kyoto University, 54 Kawaharacho Shogoin, Sakyo-ku, 606, Kyoto, Japan

    Takashi Nakamura & Masanori Oka

  3. Department of Industrial Chemistry, Faculty of Engineering, Kyoto University, 54 Kawaharacho Shogoin Sakyo-ku, 606, Kyoto, Japan

    Tadashi Kokubo

Authors
  1. Toshiaki Kitsugi
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Takao Yamamuro
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Takashi Nakamura
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Masanori Oka
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Tadashi Kokubo
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

Kitsugi, T., Yamamuro, T., Nakamura, T. et al. Influence of disodium (1-hydroxythylidene) diphosphonate on bonding between glass-ceramics containing apatite and wollastonite and mature male rabbit bone. Calcif Tissue Int 52, 378–385 (1993). https://doi.org/10.1007/BF00310203

Download citation

  • Received:

  • Revised:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF00310203

Key words

Search

Navigation