Summary
In this study we have investigated some sets of experimental conditions leading to supramolecular orientation in a triblock copolymer with cylindrical structure. The shear modulus and viscosity of the polymer of the matrix are higher than those of the polymer of the cylinders. The orientation is obtained by means of a steady simple shear strain applied to the sample at a temperature above the glass transition temperatures of the two phases. It was found that the dynamic viscoelastic properties of the material show a singular point at a particular frequency corresponding to the shear rate in steady flow leading to the destruction of the orientation.
Zusammenfassung
Es werden verschiedene Versuchsbedingungen untersucht, die zur übermolekularen Orientierung in einem Dreiblockcopolymeren mit Zylinderstruktur führen. Wenn das Polymer oberhalb der Glastemperatur der beiden Blöcke einer einfachen Scherung ausgesetzt wird, richten sich die Zylinder parallel aus, wenn die Schergeschwindigkeit unter einer gewissen Grenze bleibt. Bei einer bestimmten Schergeschwindigkeit wird die Zylinderstruktur zerstört. Die Analyse des viskoelastischen Verhaltens zeigt bei dieser Schergeschwindigkeit ebenfalls eine Besonderheit.
Similar content being viewed by others
References
Folkes, M., A. Keller, in: Physics of glassy polymers, ed.R. N. Haward, London: Applied Science Publ. (1973).
Gallot, B. R. M., Advances in Polymer Science29, 87 (1978).
Hadziioannou, G., A. Mathis, A. Skoulios, Colloid and Polymer Science.257, 136 (1979).
Terrisse, J., Thesis, University of Strasbourg (1973).
Schirrer, R., Colloid and Polymer Sci.257, 795 (1979).
Pixa, R., Thesis to be published.
Suck-Hyun, Lee, (unpublished work).
Goett, A., J. Journe, Caoutchoucs et Plastiques53, 3, 47 (1976).
Weill, A., R. Pixa, J. Polymer Sci., Polymer Symposium58, 381 (1977).
Cox, P. W., E. H. Merz, J. Polymer Sci.28, 619 (1958).
Author information
Authors and Affiliations
Additional information
With 6 figures
Rights and permissions
About this article
Cite this article
Schirrer, R., Pixa, R. Complex elastic modulus and orientation mechanisms of a triblock copolymer. Colloid & Polymer Sci 258, 802–806 (1980). https://doi.org/10.1007/BF01566234
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01566234