Abstract
Y3Fe5O12, Y3Al5O12 and Gd3Ga5O12 single crystal granets were implanted with 1017iron.cm−2. Complementary techniques: CEMS, TEM and XRD at glancing angles have allowed to follow the behavior of implanted iron during thermal annealings. For Y3Fe5O12 large α-Fe2O3 particles are formed after annealings and at 1200°C occurs a low temperature regime of the Morin transition at room temperature. For Y3Al5O12, due to aluminium substitution in the precipitates, the Morin transition is only detected after an annealing at 1300°C whereas in Gd3Ga5O12 no Morin transition is observed.
Similar content being viewed by others
References
P. Gérard F. Ravel, J.L. Ponthenier, M. Dupuy and B. Blanchard, J. Appl. Phys. 55(1984)2563.
P. Gérard, M. Madore and G. Suran, IEEE Trans. Magn. Mag. 18(1982)1274.
J.O. Artman, J.C. Murphy and S. Foner, Phys. Rev. 138A(1965)912.
P.J. Besser, A.H. Morrish and C.W. Searle, Phys. Rev. 153(1967)632.
R.W. Vaughan and H.G. Drickamer, J. Chem. Phys. 47(1967)1530.
C.L. Bruzzone and R. Ingalls, Phys. Rev. B28(1983)2430.
W. Kündig, H. Bommel, G. Constabaris and R.H. Lindquist, Phys. Rev. 142(1966)327
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Marest, G., Kornilios, N., Perez, A. et al. Morin transition in annealed iron implanted garnets. Hyperfine Interact 35, 943–946 (1987). https://doi.org/10.1007/BF02394529
Issue Date:
DOI: https://doi.org/10.1007/BF02394529