Abstract
The microhardness,H, of random copolymers of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalene-2,6-dicarboxilate) (PEN) was determined over a wide range of compositions. It is shown that microhardness of the materials is strongly affected by the composition. The mechanical property,H, of the quenched amorphous copolyester films is discussed in terms of a simple model given by the additivity values of the single componentsH PETa andH PENa . In materials containing up to 30% PEN, crystals of PET are found after annealing at temperatures 10 °C below their melting points. In materials containing ∼ 80% PEN, after annealing at about 20 °C below the melting point, crystals of PEN are formed. The observed deviation ofH for the crystallized films from the additive behaviour of the single components can be quantitatively related to two factors: the changes occurring in the crystallinity value and in the thickness of PET and PEN crystals.
Similar content being viewed by others
References
S. Buchner, D. Chen, R. Gehrke andH. G. Zachmann Molec. Cryst. Liq. Cryst. 155 (1988) 357.
F. J. Baltá Calleja, C. Santa Cruz, D. Chen andH. G. Zachmann Polymer, in press.
F. J. Baltá Calleja,Adv. Polym. Sci. 66 (1985) 117
B. Darlix, B. Monasse andP. Montmitonnet,Polym. Test. 6 (1986) 107.
B. Martín, J. M. Pereña, J. M. Pastor andJ. A. de Saja,J. Mater. Sci. Lett. 5 (1986) 1027.
D. Chen, PhD thesis, University of Hamburg (1990).
G. R. Strobl andM. J. Schneider,J. Polym. Sci. 18 (1980) 1343.
F. J. Baltá Calleja andH. G. Kilian,Colloid Polym. Sci. 266 (1988) 29.
Idem, ibid. 263 (1985) 697.
C. Santa Cruz, F. J. Baltá Calleja, H. G. Zachmann, N. Stribeck andT. Asano,J. Polym. Sci., Polym. Phys. 29 (1991) 819
F. J. Baltá Calleja, C. Santa Cruz, R. K. Bayer andH. G. Kilian Colloid Polym. Sci. 268 (1990) 440.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Santa Cruz, C., Baltá Calleja, F.J., Zachmann, H.G. et al. Mechanical properties and structure of glassy and semicrystalline random copolymers of poly(ethylene terephthalate) and poly(ethylene naphthalene-2,6-dicarboxilate). J Mater Sci 27, 2161–2164 (1992). https://doi.org/10.1007/BF01117931
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01117931