Goethite waste, originated in the hydrometallurgy of zinc, was characterized and recycled, in combination with raw materials, for producing glass-ceramic (GC) materials. Four base compositions were prepared with an Fe2O3 content ranging from 15 to 25 wt%. The mixtures were melted at 1400–1450 °C and quenched to obtain the glass. The nucleation and crystallization temperatures and the activation energy of the crystallization process were determined by differential thermal analysis. The glass samples were nucleated at 660 °C for times ranging from 1 to 4 h and crystallized at 800–900 °C for 1 to 4 h. X-ray diffraction and fluorescence analysis were performed on the glasses and GC samples and the crystalline phases characterized. The percentage of crystallinity was determined as a function of the temperature and duration of the thermal treatment. The fractional factorial experimental approach was carried out on the 20 wt% Fe2O3 composition with the aim of evaluating the influence of the nucleation temperature and time, the crystallization temperature and time and the presence of a reducing agent on the glass devitrification process.
Similar content being viewed by others
References
P. W. McMillan, “Glass ceramics” (Academic, London, 1979) p. 168.
J. Hlavac, “The technology of glass ceramics” (Elsevier, 1983).
Z. Strnad, “Glass science and technology” (Elsevier, Amsterdam, 1986) p. 110.
M. Pelino, L. Marinacci, C. Cantalini andP. P. Boattini,Advanced Ceram. Glass 4 (1992) 13.
M. Pelino, C. Cantalini, P. P. Boattini, C. Abbruzzese andJ. Ma. Rincon, in Proceedings of Austceram 92, edited by M. J. Bannister, Melbourne, August 1992, p. 1173.
M. Pelino, C. Cantalini, P. P. Boattini, C. Abbruzzese, J. Ma. Rincon andJ. E. Garcia Herandez, in proceedings of EMRS 1992 Fall Meeting, Strasbourg, November, 1992.
Idem Resources, Conservation & Recycling in press.
J. Ma. Rincon, P. Callejas andM. Romero, 2nd Semestral Report, EC Contract MA2R-CT90-000 7 (DG, XII, Bruxelles, 1993).
G. H. Beall andH. L. Ritter,Amer. Ceram. Soc. Bull. 55 (1976) 579.
M. Rutstein,Amer. Min. 54 (1968) 238.
O. L. Davies, “The design and analysis of industrial experiments” (Longman, London, 1979) p. 440.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pelino, M., Cantalini, C., Veglio', F. et al. Crystallization of glasses obtained by recycling goethite industrial wastes to produce glass-ceramic materials. J Mater Sci 29, 2087–2094 (1994). https://doi.org/10.1007/BF01154684
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01154684