Abstract
The stress corrosion cracking (SCC) initiation process for 4340 high strength steel in distilled water at room temperature was studied using a new kind of instrument: an environmental scanning electron microscope (ESEM). It was found that the applied stress accelerated oxide film formation which has an important influence on the subsequent SCC initiation. SCC was observed to initiate in the following circumstances: (1) cracking of a thick oxide film leading to SCC initiation along metal grain boundaries, (2) the initiation of pits initiating SCC in the metal and (3) SCC initiating from the edge of the specimen.
All these three SCC initiation circumstances are consistent with the following model which couples SCC initiation with cracking of a surface protective oxide. There is a dynamic interaction between oxide formation, the applied stress, oxide cracking, pitting and the initiation of SCC. An aspect of the dynamic interaction is cracks forming in a protective surface oxide because of the applied stress, exposing to the water bare metal at the oxide crack tip, and oxidation of the bare metal causing crack healing. Oxide crack healing would be competing with the initiation of intergranular SCC if an oxide crack meets the metal surface at a grain boundary. If the intergranular SCC penetration is sufficiently fast along the metal grain boundary, then the crack yaws open preventing healing of the oxide crack. If intergranular SCC penetration is not sufficiently fast, then the oxidation process could produce sufficient oxide to fill both the stress corrosion crack and the oxide crack; in this case there would be initiation of SCC but only limited propagation of SCC. Stress-induced cracks in very thin oxide can induce pits which initiate SCC, and under some conditions such stress induced cracks in a thin oxide can directly initiate SCC.
Similar content being viewed by others
References
A. Atrens and Z. F. Wang, Mater. Forum 19 (1995) 9.
T. K. Christman, Mater. Perf. 30 (1991) 23.
Idem. Corrosion 46 (1990) 450.
R. N. Parkins, in “Fundamental aspects of SCC”, edited by R. W. Staehle, A. J. Forty and D. V. Rooyen (Houston, TX, NACE, 1969) p. 361.
P. R. Rhodes, Corrosion 25 (1969) 462.
A. J. McEvily, A. P. Bond, J. Electrochem. Soc. 112 (1965) 112.
E. N. Pugh, in “The theory of SCC in alloys”, edited by J. C. Scully (NATO, Brussels, 1977) p. 21.
A. R. Troiono, “Hydrogen in Metals”, edited by I. M. Berstein, (Met. Soc. AIME, 1974) p. 12.
P. R. Rhodes, Corrosion 25 (1969) 462.
Z. F. Wang and A. Atrens, Metall. and Mater.Trans. 27A (1996) 2686.
S. Ramamurthy and A. Atrens, Corrosion Sci. 34 (1993) 1385.
M. O. Speidel, in “Corrosion in power generating equipment”, M. O. Speidel and A. Atrens (Plenum, Oxford and hb 1984) p. 85.
R. Magdowski Pedrazzoli and M. O. Speidel, in “Parkins Symposium on fundamental aspects of stress corrosion cracking”, edited by S. M. Bruemmer, E. I. Meletis, R. H. Jones, W. W. Gerberich, F. P. Ford and R. W. Staehle (TMS, Warrendale, Pennsylvania 1992) 341.
S. Jin and A. Atrens, Appl. Phys. A2 42 (1987) 149.
Idem., ibid. 50 (1990) 287.
A. S. Lim and A. Atrens, ibid. 53 (1992) 273.
Idem., ibid. 54 (1992) 500.
Z. F. Wang and A. Atrens J. Mater. Sci. Accepted for publication.
Idem., ibid. J. Mater. Sci.
A. Atrens, Z. F. Wang, N. Kinaev, D. R. Cousens and J. Q. Wang, in Proceedings of 13 International Corrosion Congress, Melbourne (1996).
A. Oehlert and A. Atrens, Mater. Forum 17 (1993) 415.
Idem. Corrosion Sci. 38 (1996) 1159.
A. Atrens, C. C. Brosnan, S. Ramamurthy, A. Oehlert and I. O. Smith, Measurement Sci.Technol. 4 (1993) 1281.
S. Ramamurthy and A. Atrens, Corrosion Sci. 34 (1993) 1385.
A. Atrens and A. Oehlert, J. Mater. Sci. submitted.
J. Salmond and A. Atrens, Scripta Metall. Mater. 26 (1992) 1447.
R. M. Rieck, A. Atrens and I. O. Smith, Met. Trans. 20A (1989) 889.
A. Oehlert and A. Atrens, Overview No 114 Acta Metall. Mater. 42 (1994) 1493.
A. Atrens, R. M. Reick and I. O. Smith, in “ICF7 Advances in Fracture Research”, edited by K. Salama, K. Ravi-Chandar, D. M. R. Taplin and P. Rama Rao (Pergamon Press, Oxford, 1989) p. 1603.
A. Oehlert and A. Atrens, J. Mater. Sci. 32 (1977) in press.
R. M. Rieck, A. Atrens and I. O. Smith, Mater. Forum. 13 (1989) 48.
Idem., ibid. 13 (1989) 54.
J. D. Gates, A. Atrens and I. O. Smith, Z. furYerkstofftechnik 18 (1987) 165.
Idem., ibid 18 (1987) 179.
Idem., ibid 18 (1987) 344.
J. Skogsmo and A. Atrens, Acta Metall. Mater. 42 (1994) 1139.
S. Ramamurthy, A. Atrens, I. O. Smith, Mater. Sci. Forum 44 & 45 (1989) 139.
A. Atrens, R. Coade, J. Allison, H. Kohl, G. Hochertler and G. Krist, Mater. Forum 17 (1993) 263.
P. J. R. Uwins, ibid. 18 (1994) 51.
N. N. Kinaev, A. Atrens, D. R. Cousens and R. Miller, in Proceedings of 14th Australian Conference on Electron Microscopy, Sydney (1996) A95.
A. Atrens, Z. F. Wang, N. Kinaev, D. R. Cousens and J. Q. Wang, in Proceedings of 13 International Corrosion Congress, Nov 1996, Melbourne.
R. N. Parkins, E. Belhimer and W. K. Blanchard Jr, Corrosion 49 (1993) 951.
R. N. Parkins, W. K. Blanchard Jr, B. S. Delanty, ibid. 50 (1994) 395.
H. R. Baker, C. R. Singleterry, ibid. 28 (1972) 340.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Atrens, A., Wang, Z.F. ESEM observations of SCC initiation for 4340 high strength steel in distilled water. Journal of Materials Science 33, 405–415 (1998). https://doi.org/10.1023/A:1004328031430
Issue Date:
DOI: https://doi.org/10.1023/A:1004328031430