Abstract
The influence of KclO 3 addition on the AC complex susceptibility (χac) and microstructural morphology of YBCO HTSC with nominal composition Y (1−0.2x) Ba (2−0.2x) K x Cu 3 O y (x = 0 ÷ 0.40) were investigated. Xac was recorded as a function of temperature and of the concentration of KClO 3 in various AC magnetic fields up to 19 Oe. The data were analyzed using the relation h = a(1 − T m /T c ) n . The results obtained showed that the presence of K- and Cl-containing impurities on the grain boundaries change the intergranular coupling and, within certain concentration limits, improves the superconducting parameters.
Similar content being viewed by others
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Veneva, A., Koblischka, M.R., Sakai, N. et al. Influence of KClO3 Addition on the Magnetic Properties and Microstructural Morphology of Y(1−0.2x)Ba(2−0.2x)KxCu3Oy (x = 0 ÷ 0.40) Polycrystalline HTSC. Journal of Low Temperature Physics 117, 939–943 (1999). https://doi.org/10.1023/A:1022515310847
Issue Date:
DOI: https://doi.org/10.1023/A:1022515310847