Abstract
Recent superconductivity and crystallographic data for the MM′X ternary compounds with M = Ti, Zr, or Hf, M′ = Ru or Os, and X = P or As are presented. Moderate to high superconducting transition temperatures (T c 's)are exhibited by the ZrRuSi-type hexagonal phase which is found to be metastable at low temperatures. The low-temperature phase of ZrRuP has the TiNiSi-type orthorhombic structure and exhibits superconductivity at 3.9K. The low-temperature phase of HfRuAs has the TiFeSi-type orthorhombic superstructure and remains normal at 1.0K. TiRuAs exists only with the superstructure and remains normal at 0.35K. The details of these various structural modifications point to the importance of undistorted zig-zag chains of metal atoms for the occurrence of superconductivity in these compounds. The lowT c for TiRuP and the absence of superconductivity for TiOsP above 0.35K are not accounted for by these structural modifications.
Similar content being viewed by others
References
G.P. Meisner: Thesis, Univeristy of California, San Diego (1982)
H. Barz, H.C. Ku, G.P. Meisner, Z. Fisk, B.T. Matthias: Proc. Natl. Acad. Sci. USA77, 3132 (1980)
G.P. Meisner, H.C. Ku, H. Barz: Mater. Res. Bull.18, (in press)
V. Johnson, W. Jeitschko: J. Solid State Chem.4, 123 (1972)
R. Fruchart, A. Roger, J.P. Sénateur: J. Appl. Phys.40, 1250 (1969); Ann. Chim.4, 79 (1960)
A. Roger: Thesis, University of Paris, Orsay (1970)
J. Roy-Montreuil, B. Deyris, A. Michel, R. Fruchart, J.P. Sénateur, D. Boursier: Ann. Chim. Fr.4, 411 (1979)
J.B. Goodenough: J. Solid State Chem.7, 428 (1973)
G.P. Meisner: Phys. Lett. A406, (in press)
G.R. Stewart, G.P. Meisner, H.C. Ku: InSuperconductivity in d- and f-Band Metals 1982, ed. by W. Buckel and W. Weber (Kernforschungszentrum Karlsruhe GmbH, Karlsruhe 1982) p. 331
G. Maronneau: Compt. Rend.130, 657 (1900)
A.J.P. Meyer, M.C. Cadeville: J. Phys. Soc. Jpn.17, B-I 223 (1962)
At the composition indicated the Cu-P flux is near a eutectic between Cu and Cu3P having a melting point of 714°C. See: M. Hansen,The Constitution of Binary Alloys (McGraw-Hill, New York 1958) p. 607
Intensity calculations were performed using the “Lazy Pulverix” computer program. [K. Yvon, W. Jeitschko, E. Parthé: J. Appl. Crystallogr.10, 73 (1977)]
The possibility of an ordering inversion for TiRuP was suggested by Dr. D. C. Johnston (private communication)
G.P. Meisner, H.C. Ku: InTernary Superconductors, ed. by G.K. Shenoy, B.D. Dunlap, F.Y. Fradin (North-Holland, Amsterdam 1981) p. 255
C.B. Shoemaker, D.P. Shoemaker: Acta Crystallogr.18, 900 (1965)
S. Rundqvist, P.C. Nawapong: Acta Chem. Scand.20, 2250 (1966)
W. Höme, K. Yvon, H.F. Braun, G.P. Meisner, H.C. Ku: To be published
W. Jeitschko: Acta Crystallogr. B26, 815 (1970)
P.I. Kripjakavic, V.Ja. Markiv, Ja.V. Melnyk: Dopov. Akad. Nauk. Ukr. RSR A29, 750 (1967)
A.E. Dwight, M.H. Mueller, R.A. Conner, Jr., J.W. Downey, H. Knott: Trans. Am. Inst. Min. (Metall.) Eng.242, 2705 (1968)
D.C. Johnston, H.F. Braun: InSuperconductivity in Ternary Compounds II, ed. by M.B. Maple and Ø. Fischer. Topics in Current Physics34 (Springer, Berlin, Heidelberg, New York 1982) pp. 11–55
J. Ball, D.C. Johnston: Unpublished
E. Hovestreydt, N. Engle, K. Klepp, B. Chabot, E. Parthé: J. Less-Common Met.85, 247 (1982) and references therein
The data for the MM′ binary compounds were taken from: W.B. Pearson:A Handbook of Lattice Spacings and Structures of Metals and Alloys, Vol. 2 (Pergamon Press, Oxford 1967)
W.H. Zachariasen: J. Inorg. Nucl. Chem.35, 3487 (1973)