Armco iron samples were surface nitrided by irradiating them with pulses of an excimer laser in a nitrogen atmosphere. The resulting nitrogen depth profiles measured by Resonant Nuclear Reaction Analysis (RNRA) and the phase formation determined by Conversion Electron Mössbauer Spectroscopy (CEMS) were investigated as functions of energy density and the number of pulses. The nitrogen content of the samples was found to be independent of the number of pulses in a layer of 50 nm from the surface and to increase in depths exceeding 150 nm. The phase composition did not change with the number of pulses. The nitrogen content can be related to an enhanced nitrogen solubility based on high temperatures and high pressures due to the laser-induced plasma above the sample. With increasing pulse energy density, the phase composition changes towards phases with higher nitrogen contents. Nitrogen diffusion seems to be the limiting factor for the nitriding process.
Similar content being viewed by others
References
E. Schubert, H. W. Bergmann: Lasers Eng.2, 111 (1993).
S. B. Ogale: Thin Solid Films163, 215 (1988).
Z. S. Yu. Z. K. Quan: Mater. Chem. Phys.25, 277 (1990)
A. L. Galiev, L. L. Krapivin, A. A. Uglov: Sov. Phys. Dokl.25, 208 (1980)
A. A. Uglov, M. B. Ignatev, I. Y. S. A. G. Gnedovets: J. Phys. (Paris)50, C5 (1989)
E. D'Anna, G. Leggieri, A. Luches, M. Martino, A. V. Drigo, I. N. Mihailescu, S. Ganatsios: J. Appl. Phys.69, 1687 (1991)
E. D'Anna, M. L. De Giorgi, G. Leggieri, A. Luches, M. Martino, A. Perrone, I. N. Mihailescu, P. Mengucci, A. V. Drigo: Thin Solid Films213, 197 (1992)
K. Nakamura, M. Hikita, H. Asano, A. Terada: Jpn. J. Appl. Phys.21, 672 (1982)
I. Ursu, I. N. Mihailescu, L. C. N. V. S. Teodorescu, A. M. Prokhorov, V. I. Konov, S. A. Uglov, J. Phys. D20, 1519 (1987)
VDI-Lexikon Werkstofftechnik (VDI, Düsseldorf 1990)
D. L. Williamson: Nucl. Instrum. Methods B76, 262 (1993)
P. Schaaf, A. Emmel, C. Illgner, K. P. Lieb, E. Schubert, H. W. Bergmann: Mater. Sci. Eng. Lett. A (1995) (in press)
P. Schaaf, A. Krämer, L. Blaes, G. Wagner, F. Aubertin, U. Gonser: NucI. Instrum. MethodsB53, 184 (1991)
P. Schaaf, A. Emmel, E. Schubert, H. W. Bergmann, K. P. Lieb: Hyperfine Interact.92, 1361 (1994)
W. Kündig: Nucl. Instrum. Methods75, 336 (1969)
P. Schaaf, U. Gonser: Hyperfine Interact.57, 2101 (1990)
T. Osipowicz, K. P. Lieb, S. Brüssermann: Nucl. Instrum. Methods B18, 232 (1987)
M. Uhrmacher, K. Pampus, F. Bergmeister, D. Purschke, K. P. Lieb: Nucl. Instrum. Methods B9, 234 (1985)
M. Borowski, C. Illgner, T. Kacsich, K. P. Lieb, P. Schaaf: Unpublished
R. C. Ruhl, M. Cohen: Trans. Metall. Soc. AIME245, 241 (1969)
H. A. Wriedt, N. A. Gokcen, R. H. Nafziger: Bull. Alloy Phase Diag.8, 355 (1987)
P. Schaaf, C. Illgner, M. Niederdrenk, K. P. Lieb: Hyperfine Interact.95, 199 (1995)
N. DeChristofaro, R. Kaplow: Metall. Trans. A8, 35 (1977)
Y. S. Touloukian, R. W. Powell, C. Y. Ho, P. G. Klemens: In:Thermal Conductivity, Metallic Elements and Alloys, ed. by Y. S. Touloukian, C. Y. Ho, Thermophysical Properties of Matter, Vol. 1, (IFI/Plenum, New York 1970)
Y. S. Touloukian, R. W. Powell, C. Y. Ho, M. C. Nicolaou: InThermal Diffusivity, ed. by Y. S. Touloukian, C. Y. Ho, Thermophysical Properties of Matter, Vol. 10 (IFI/Plenum, New York 1973)
L. M. Lyamshev: Sov. Phys. Usp.24, 977 (1981)
R. C. Weast, M. J. Astle (eds.):CRC Handbook of Chemistry and Physics, (CRC, Boca Raton, FL 1982)
J. Kunze:Nitrogen and Carbon in Iron and Steel (Akademie, Berlin 1990)