Summary
The visible absorption spectra, the electron microphotographs and the optical microphotograph of the cellulosic fibres dyed with direct dyes were observed in comparison with Acridine Orange free base (AO). Furthermore, dyeing was carried out in a thermostat bath at 90 ± 1, 80 ± 1, and 70 ± 1 °C. From the results, the change of enthalpy,ΔH° for the dyeing was calculated.Δh° of AO was very small in comparison with other direct dyes, and AO in the cellulosic fibres has predominantly crystallized property. The result was expressed as follows: Crystallized tendency =(dye-dye interaction) -(dye-fibre interaction).
Zusammenfassung
Die Absorptionsspektren, elektronenmikroskopische Aufnahmen und Photographien von mit Direkt-Farbstoff gefärbten Celluloe-Fasern im Vergleich zu mit Acridine Orange als freie Base (AO) wurden angefertigt. Die Färbung wurde für Temperaturen von 90 ± 1, 80 ± 1 und 70 ± 1 °C ausgeführt. Die Änderung der molaren Enthalpie ΔH° wurde daraus berechnet. Die Werte von ΔH° mit Acridine Orange sind sehr niedrig im Vergleich mit anderen Direkt-Farbstoffen. Und das AO zeigt in den Zellulosefasern eine sehr große Tendenz zur Kristallisation. Dies ist folgendermaßen zu verstehen: Kristall-Tendenz bedeutet hohe Farbstoff-Farbstoff Wechselwirkung und damit auch hohe Farbstoff Faser Wechselwirkung.
Similar content being viewed by others
References
Ohtsu, T., K. Nishida, K. Nagumo, K. Tsuda, Kolloid-Z. u. Z. Polymere249, 1077 (1971).
Ohtsu, T., K. Nishida, K. Nagumo, K. Tsuda, ibid,250, 860 (1972).
Ohtsu, T., K. Nishida, K. Nagumo, K. Tsuda, ibid,252, 377 (1974).
Ohtsu, T., K. Nishida, K. Tsuda, Progr. Colloid & Polymer Sci.,58, 141 (1970).
Ohtsu, T., K. Nishida, K. Tsuda, Meeting of: Fibre Science and Technology (Tokyo 1975).
Robinson, C., H. A. Mills, J. Proc. Roy. Soc. (London)A131, 576 (1931).
Doree, C., The methods of cellulose chemistry, 2nd ed. p. 2 (London 1950).
Giles, C. H., A laboratory course in dyeing, 2nd ed. p. 63 (Yorkshire 1971).
Ohtsu, T., K. Nishida, I. Watanabe, Colloid & Polymer Sci.252, 65 (1974).
Bach, H., Angew. Chem.75, 407 (1963).
Vickerstaff T., The physical chemistry of dyeing, 2nd ed., p. 118 (London 1954).
Author information
Authors and Affiliations
Additional information
With 6 figures and 1 table
Rights and permissions
About this article
Cite this article
Toda, T., Nishida, K. & Tsuda, K. Aggregates or crystals of direct dyes within the void places of cellulosic fibres. Colloid & Polymer Sci 255, 1110–1113 (1977). https://doi.org/10.1007/BF01549897
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01549897