Stoichiometry and superconductivity in single layer Bi2+xSr2−yCuO6+-δ

https://doi.org/10.1016/0921-4534(91)90791-VGet rights and content

Abstract

An insulating polymorph with a composition close to Bi2Sr2CuO6 complicates the synthesis of the single copper layer superconductor Bi2+xSr2−yCuO6±δ. We concentrate on the region where the material is single phase in air synthesis (2.18 < x < 2.29, 1.44 < y < 1.7). The physical properties from insulating to marginally conducting as the composition moves toward x = y = 0. Like to two-layer compound, the material has a superlattice due to a buckling of the planar structure, however the superlattice coherence is degraded by defects at finite values of x and y. Density measurements indicate that the nonstoichiometry of Bi2+xSr2−y CuO6±δ is not accompanied by the formation of a large number of vacancies. The insulating polymorph, Bi2Sr2CuO6, can be suppressed by synthesis in modest oxygen pressures (above 5–10 atm). The result is a bulk superconductor (Tc ≈ 10 K).

References (33)

  • Y. Ikeda et al.

    Physica C

    (1989)
  • J.B. Torrance et al.

    Solid State Commun.

    (1988)
  • P. Strobel et al.

    Physica C

    (1988)
  • R.J. Cava et al.

    Physica C

    (1990)
  • R.J. Cava, B. Batlogg, R.B. van Dover, J.J. Krajewski, J.V. Waszczak, R.M. Fleming, W.F. Peck Jr., L.W. Rupp Jr., P....
  • M. Onoda et al.

    Jpn. J. Appl. Phys.

    (1988)
  • S. Martin et al.

    Phys. Rev.

    (1990)
  • A.T. Fiory et al.

    Phys. Rev.

    (1990)
  • C. Michel et al.

    Z. Phys. B

    (1987)
  • J. Akimitzu et al.

    Jpn. J. Appl. Phys.

    (1987)
  • G. Xiao et al.

    Phys. Rev.

    (1988)
  • J.M. Tarascon et al.

    Phys. Rev.

    (1988)
  • M.T. Casais et al.
  • H. Sawa et al.

    Jpn. J. Appl. Phys.

    (1988)
  • C.C. Torardi et al.

    Phys. Rev.

    (1988)
  • B.C. Chakoumakos et al.E. Sonder et al.

    Phys. Rev.

    (1989)
  • Cited by (58)

    • Substitution of Sr<sup>2+</sup> by Eu<sup>3+</sup> in Bi-2201 ceramics, effects on structure and physical properties

      2010, Solid State Sciences
      Citation Excerpt :

      The two phases (A and B) are easily distinguished from the XRD patterns. The B phase has a peak about 2θ ≈ 25.79°, representing the (113) line, whereas the A phase has no reflection at this position but a peak at 2θ ≈ 26.76° (–315) as well as other peaks in the range 20°–30° not observed and not indexable in B phase [3,7]. In addition to the main lines (hkl), some satellite reflections related to the modulation of the structure are observed in the doped samples.

    • Suppression of modulations in fluorinated Bi-2201 phases

      2001, Journal of Solid State Chemistry
    View all citing articles on Scopus
    View full text