Abstract
MnAl-X (X=Ti, Cu, Ni, C, B) ribbons were fabricated by a rapid quenching from the melt using a single roller method. As-rapid quenched ribbons were quenched completely into high temperature h c p phase. The rapid quenched ribbons were brittle especially carbon doped ribbons, however, the titanium doped ribbons were relatively ductile. Hard magnetic properties were measured using a vibrating sample magnetometer for the ten kinds of ribbons annealed at 410–700° C for 10 min–100 h. Phase transformation characteristics and magnetic properties were discussed by comparison with the samples produced by the conventional method. Titanium, boron and carbon doped ribbons showed good hard magnetic properties.
Similar content being viewed by others
References
A. J. J. Koch, P. Hokkeling, M. G. V. D. Steeg and K. J. De Vos, J. Appl. Phys. 31 (1960) 75S.
H. Kono, J. Phys. Soc. Jpn 13 (1958) 1444.
J. J. Van Den Broek, H. Donkersloot, G. Van Tendeloo and J. Van Landuyt, Acta Met. 27 (1979) 1497.
W. H. Dreizler and A. Menth, IEEEE Trans. Mag. MAG-16 (1980) 534.
T. Ohtani, N. Kato, S. Kojima, K. Kojima, Y. Sakamoto, I., Konno, M. Tsukahara and T. Kubo, ibid. MAG-13 (1977) 1328.
S. Kojima, J. Mag. Soc. Jpn 6 (1982) 18.
Z. A. Abdelnour, H. F. Mildrum and K. J. Strnat, IEEE Trans. Mag. MAG-17 (1981) 2651.
A. Inoue, T. Masumoto and H. Tomioka, J. Mater. Sci. 19 (1984) 3097.
R. H. Willens, IEEE Trans. Mag. MAG-16 (1980) 1059.
M. Takahashi and T. Miyazaki, J. Mag. Soc. Jpn 6 (1982) 22.
A. E. Berkowitz, J. D. Livingston and J. L. Walter, J. Appl. Phys. 55 (1984) 2106.
T. Kawaguchi, M. Nagakura, K. Kamino and S. Yoshizawa, Nippon Kinzoku Gakkaishi 28 (1964) 384.
K. Kamino, ibid. 30 (1966) 636.
P. B. Braun and J. A. Goedkoop. Acta Cryst. 16 (1963) 737.
Y. Yang, W. Ho, C. Lin, J. Yang, H. Zhou, J. Zhu, X. Zeng, B. Zhang and L. Jin, J. Appl. Phys. 55 (1984) 2053.
H. Kaneko, T. Nishizawa and M. Homma, Nippon Kinzoku Gakkaishi 31 (1967) 1331.
E. L. Houseman and J. P. Jakubovics, J. Mag. Mag. Mater. 31–34 (1983) 1005.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sakka, Y., Nakamura, M. & Hoshimoto, K. Rapid quenching and properties of hard magnetic materials in MnAl-X (X=Ti, Cu, Ni, C, B) systems. J Mater Sci 24, 4331–4338 (1989). https://doi.org/10.1007/BF00544507
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00544507