Abstract
The electrical degradation phenomena of zinc oxide-based varistors were studied using a high-energy current pulse and a.c. polarization at different temperatures. Activation energy measurements during the degradation process showed that these phenomena are associated with diffusion and that the diffusion-controlling species are slower than Zn., For degradation promoted by current pulses of 8×20 μs, the Schottky potential barrier deformation was measured. A decrease in height and width of the potential barrier due to the reduction of surface states density,N s, without a significant change in donor density,N d, was observed. To explain these results, a modification of the unstable components model is proposed for the potential barrier in which the degradation is due to oxi-reduction reactions between atomic defects. These reactions promote the elimination of zinc vacancies and/or adsorbed oxygen on the grain boundaries.
Similar content being viewed by others
References
T. K. Gupta andW. G. Carlson,J. Appl. Phys. 52 (1981) 4104.
C. G. Shirley andW. M. Paulson,ibid. 50 (1979) 5782.
T. K. Gupta andW. G. Carlson,J. Mater. Sci. 20 (1985) 3487.
Idem., “Additives and Interfaces in Electronic Ceramics”, in “Advances in Ceramics”, Vol. 7, edited by F. M. Yan and H. H. Heuer (American Ceramic Society, Columbus, Ohio, 1983) p. 30.
D. Binesti, PhD thesis, University of Bordeaux I, Bordeaux, France (1985).
H. R. Philipp andL. M. Levinson, in “Additives and Interfaces in Electronics Ceramics, Advances in Ceramics”, Vol. 7, edited by M. F. Yam and H. H. Heuer (American Ceramic Society, Columbus, Ohio, 1983) p. 1.
K. Eda,J. Appl. Phys. 49 (1978) 2964.
R. A. Swalin, “Thermodynamics of Solids” (Wiley, New York, 1964).
W. Heywang,J. Amer. Ceram. Soc. 47 (1964) 484.
B. Tanouti, PhD thesis, University of Bordeaux I, Bordeaux, France (1985).
S. A. Pianaro, Ms thesis, UFSCar, São Carlos (1990).
A. Smith, J. F. Baunard, P. Abetard andM. F. Denarot,J. Appl. Phys. 65 (1989) 5119.
S. Fujitsu, K. Koumoto andH. Yanagida,Solid State Ionics 32/33 (1989) 482.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Leite, E.R., Varela, J.A. & Longo, E. A new interpretation for the degradation phenomenon of ZnO varistors. J Mater Sci 27, 5325–5329 (1992). https://doi.org/10.1007/BF02403838
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02403838