Abstract
The location of the monovariant eutectic trough extending from the binary eutectic Cu-Cu2Mg into the Cu-Mg-Ni ternary alloy system has been established for alloys containing up to 25 at.% Ni. Liquidus and solidus temperatures along this eutectic trough were determined by thermal analysis. Microscopic and electron microprobe analyses confirm the existence of a peritectic reaction in the Cu2Mg-Ni2Mg quasibinary system and establish its participation in the ternary system. The foregoing, together with data from earlier literature, allow the equilibrium phase relationships for the entire Cu-Mg-Ni ternary system to be estimated.
Similar content being viewed by others
References
V. I. Mikheeva and G. G. Babayan, Acad. Sci. USSR Proc. 108 (1956) 327.
W. Koster, Z. Metallk. 42 (1951) 326.
K. Lieser and H. Witte, ibid 43 (1952) 396.
M. Hansen, “Constitution of Binary Alloys”, 2nd edition (McGraw Hill, New York, 1958).
G. Masing, “Ternary Systems” (Dover, New York, 1960).
W. Christian, W. Hume-Rothery, and W. B. Pearson, “Metallurgical Equilibrium Diagrams” (Chapman and Hall, London, 1952).
F. N. Rhines, “Phase Diagrams in Metallurgy” (McGraw Hill, New York, 1958).
W. B. Pearson, “Handbook of Lattice Spacings and Structure of Metals”. Vol. 1 (Pergamon Press, London, 1958).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fehrenbach, P.J., Kerr, H.W. & Niessen, P. The constitution of Cu-Ni-Mg alloys. J Mater Sci 7, 1168–1174 (1972). https://doi.org/10.1007/BF00550200
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00550200