Abstract
Oxidation studies were conducted on plasma sprayed coatings of Ni-20Cr-12.5Al containing one of the following: 1% MgO, 1% La2O3, 1% Y2O3, and 0.8% Y. The alloy powders containing dispersed oxides were prepared by a variety of processes employing attrition and ball milling. The TEM characterization of the plasma sprayed deposits of Ni-20Cr-12.5Al-1Y2O3 indicated that the oxide particles ranged from almost pure aluminum oxide to various compounds of aluminum and yttrium oxide. In cyclic tests conducted at 1150 and 1225°C, the coating containing 1% Y2O3 appeared to provide the best oxidation resistance. The oxidation resistance appeared to be influenced by the size and distribution of the oxide particles.
Similar content being viewed by others
References
D. P. Whittle and J. Stringer,Phil. Trans. R. Soc. (Lond.) A295, 309 (1980).
J. R. Rairden,Thin Solid Films,53, 251 (1978).
R. C. Elam, G. W. Goward, and R. J. Hecht, US Patent No. 3928026 (December 23, 1975).
H. Nagai and M. Okabayashi,Trans. Japan Inst. Met. 22, 101 (1981).
C. S. Giggins and F. S. Pettit,Metall. Trans. 2, 1071. (1971).
J. Stringer, B. A. Wilcox, and R. I. Jaffe,Oxid. Met. 5, 11 (1972).
C. E. Lowell and W. A. Sanders,Oxid. Met. 5, 205 (1972).
J. S. Bejamin,Met. Trans.,1, 2943 (1970).
T. A. Ramanarayanan, M. Raghavan, and R. Petkovic-Luton,J. Electrochem. Soc. 131, 923 (1984).
I. M. Allam, D. P. Whittle, and J. Stringer,Oxid. Met. 13, 381 (1979).
J. R. Rairden, Private Communication.
J. R. Rairden and E. M. Haebach,Thin Solid Films,83, 353 (1982).
G. Cliff and G. Lorimer,J. Microscopy,103, 203 (1975).
M. Ragharan, J. W. Steeds, and R. Petkovic-Luton,Met. Trans. A 13A, 953 (1982).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Luthra, K.L., Hall, E.L. High temperature oxidation of Ni-20Cr-12.5Al coatings containing 1% dispersed oxides. Oxid Met 26, 385–396 (1986). https://doi.org/10.1007/BF00659343
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00659343