Fundamental absorption edge of evaporated amorphous WO₃ films

Abstract

The fundamental absorption edge of evaporated WO₃ films is investigated. The optical gap of the virgin film is estimated to be 3.41 eV at room temperature and it decreases with increase of annealing temperature up to 200°C. Annealing at 300°C leads to change in the spectral shape, which is caused by crystallization. For the films annealed at 200°C, temperature coefficient of the optical gap is estimated to be −2×10⁻⁴ eV/K and the slope of Urbach's tail is found to be independent of measuring temperature up to 200°C. With electrolytic coloration, shift of the optical gap toward higher energy is observed. Magnitude of this shift is estimated to be 0.05 eV at the color center concentration of 7.5×10²¹ cm⁻³ when H⁺ electrolyte is used. If Li⁺ electrolyte is used, the magnitude of this shift is about three times larger than in the case of H⁺ electrolyte. This fact is interpreted by a small change in the host matrix structure owing to the injection of proton or Li⁺ during coloration.