Synthesis and crystal structure of monoclinic Fe₂(SeO₄)₃

Summary

Crystals of monoclinic Fe₂(SeO₄)₃ were synthesized under hydrothermal conditions. The structure was determined by single crystal X-ray methods and refined in space group P2₁/n with 2 646 independent reflections (sin θ/λ<0.7 Å⁻¹) toR=0.033,R _w=0.037:a=8.530 (2) Å,b=8.888 (2) Å,c=11.952 (2) Å, β=91.13 (1)°,V=906.0 ų,Z=4. The crystal structure is isotypic with the monoclinic modification of Fe₂(SO₄)₃, containing two different Fe(III) and three Se(VI) atomic positions. The FeO₆ and SeO₄ polyhedra are only slightly distorted, the mean Fe-O bond lengths are 1.986 Å and 2.004 Å, the average distances within the SeO₄ tetrahedra are each 1.628 Å. The isolated FeO₆ octahedra only share corners with SeO₄ tetrahedra to build a framework structure.

Zusammenfassung

Kristalle von monoklinem Fe₂(SeO₄)₃ wurden unter Hydrothermalbedingungen gezüchtet. Die Struktur wurde mit Einkristall-Röntgenmethoden bestimmt und in der Raumgruppe P2₁/n mit 2 646 unabhängigen Reflexen (sin θ/λ<0.7Å⁻¹) aufR=0.033,R _w=0.037 verfeinert:a=8.530(2) Å,b=8.888(2) Å,c=11.952(2) Å, β=91.13(1)°,V=906.0 ų,Z=4. Die Kristallstruktur ist isotyp mit der monoklinen Modifikation von Fe₂(SO₄)₃, sie enthält zwei unterschiedliche Fe(III) und drei Se(VI) Atompositionen. Die FeO₆-Polyeder sind nur gering verzerrt, die mittleren Fe-O Bindungslängen sind 1.986 Å und 2.004 Å, die mittleren Abstände in den SeO₄-Tetraedern sind jeweils 1.628 Å. Die isolierten FeO₆-Oktaeder sind nur über gemeinsame Ecken mit SeO₄-Tetraedern verbunden, wobei eine Gerüststruktur entsteht.