Composite materials based on ultrahigh-molecular-weight polyethylene (UHMWPE)–low- molecular-weight polyethylene (LMWPE) and carbon black (CB) particles were prepared by a gelation/crystallization process from dilute solution. The method was developed to obtain composite materials with an improved and reproducible positive temperature coefficient (PTC) effect. Drastic improvement of the PTC effect was achieved when specimens with a LMWPE/UHMWPE composition of 9/1 containing 13 wt% CB were treated at 170 °C without restraint before measurement. The maximum PTC intensity, defined as the ratio of the maximum resistivity to the resistivity at room temperature, was about 5 orders of magnitude, which equals that of the LMWPE-CB system prepared by a kneading method. Interestingly, electrical resistivity during the heating-cooling process showed good reproducibility in the temperature range 30–190 °C, but has never been reported before even for cross-linked LMWPE-CB compostie. Scanning electron micrographs revealed that CB particles were dispersed in the LMWPE matrix, but not on the UHMWPE fibrils. It turns out that the network structure of UHMWPE, with a very low melt index, plays an important role in removing the negative temperature coefficient effect usually observed for the LMWPE-CB system and in ensuring the quality and the reproducibility of the PTC effect.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 31 August 1998 Accepted in revised form: 4 January 1999
Rights and permissions
About this article
Cite this article
Bin, Y., Xu, C., Agari, Y. et al. Morphology and electrical conductivity of ultrahigh-molecular-weight polyethylene–low-molecular-weight polyethylene–carbon black composites prepared by gelation /crystallization from solutions. Colloid Polym Sci 277, 452–461 (1999). https://doi.org/10.1007/s003960050408
Issue Date:
DOI: https://doi.org/10.1007/s003960050408