Role of ion beam assisted deposition in the synthesis and fracture of metal-ceramic multilayers

https://doi.org/10.1016/S0257-8972(94)80012-XGet rights and content

Abstract

Multilayer metal-ceramic films have the potential to serve as strong, tough and environmentally resistant films and coatings for a wide variety of applications. They derive their properties from the multilayer structure (architecture), the microstructure and, hence, mechanical properties of the individual layers and the stress state of the film. However, in order to realize the potential of microlaminates, these features (architecture, microstructure and stress) must be controlled. Ion beam assisted deposition (IBAD) holds the promise to provide this control. In an effort to understand how IBAD can control mechanical properties of films, single trilayer and five-bilayer metal-ceramic, Al-Al2O3 films were fabricated on ductile metal substrates using IBAD over a range of thicknesses and normalized energies. Results of bending and tension experiments revealed that the stress state is critical in determining the fracture strain (ductility) of the film. A residual compressive stress is beneficial and can be formed in the oxide phase by bombardment of the film with Ar during deposition. The behavior of film stress correlates well with Ar gas incorporation and the film consists of a high density of small cavities. Gas incorporation into the cavities or the surrounding matrix may be responsible for the observed residual compressive stress. The density of surface cracks at high strains is a function of the film architecture, film strength and the interfacial shear strength. Use of a multilayer structure reduces the crack density over a monolithic oxide film by increasing the strain needed to form through-thickness cracks and by increasing the intrinsic strength of the brittle layers by decreasing their thickness. Ion bombardment of the metal layers resulted in radiation damage and grain size refinement, both of which result in a stronger film and a lower crack density. It was shown that architecture, microstructure and stress are the key ingredients in microlaminate properties and are uniquely controllable by IBAD.

References (18)

  • A.G. Evans et al.

    Acta Metall.

    (1986)
  • B. Budiansky et al.

    J. Mech. Phys. Solids

    (1988)
  • G.R. Odette et al.

    Acta Metall.

    (1992)
  • H.C. Cao et al.

    Acta Metall.

    (1989)
  • M.Y. He et al.

    Acta Metall. Mater.

    (1993)
  • J.A. Thornton et al.

    Thin Solid Films

    (1979)
  • D.C. Agrawal et al.

    Acta Metall.

    (1989)
  • D.C. Agrawal et al.

    Mater. Sci. Eng.

    (1990)
  • V. Dietz et al.

    Nucl. Instrum. Methods B

    (1991)
There are more references available in the full text version of this article.

Cited by (9)

  • Effect of volume fraction on mechanical properties of Zr/ZrN multilayer systems

    2016, Ceramics International
    Citation Excerpt :

    In both cases values of Set 100 were better than those of Set 200. In general, the mechanical properties were improved with decrease on modular period, in good agreement with other reports [3–12]. It can be observed that hardness values are closely related with volume fraction of metallic and ceramic phases.

  • Positron annihilation lifetime measurement and X-ray analysis on 120 MeV Au<sup>+7</sup> irradiated polycrystalline tungsten

    2015, Journal of Nuclear Materials
    Citation Excerpt :

    The thermal diffusivity value of pristine and irradiated tungsten specimen are very close to each other. In solids, the total thermal conductivity is sum of electronic and lattice thermal conductivity and in case of tungsten, at room temperature, electronic thermal conductivity is dominant [44]. In solids, heat is transported by entropy (spin and charge of electron) and electric current by charge alone [45].

  • Niobium-niobium oxide multilayered coatings for corrosion protection of proton-irradiated liquid water targets for [<sup>18</sup>F] production

    2015, Thin Solid Films
    Citation Excerpt :

    The toughness enhancement is realized through the following three main mechanisms: crack deflection at interface between layers, ductile interlayer ligament bridging and crack tip blunting due to nanoplasticity at the interface. It was realized for the number of metal–ceramic multilayer systems [10–12]. Thereby Nb/Nb2O5 multilayer coatings were put forward with the aim to avoid the problem of the oxide brittleness.

View all citing articles on Scopus
View full text