On the Crystal Chemistry of a New Barium Rare-Earth Oxozincate: Ba2Er2Zn8O13High temperature reactions led to single crystals of Ba2Er2Zn8O13. It crystallizes with orthorhombic symmetry, space group C122v—Cmc21, a = 6.276, b = 10.871, c = 10.195 Å, Z = 2. The hitherto unknown crystal structure shows Zn2+ with tetrahedral, Er3+ octahedral and Ba2+ cuboctahedral coordination by O2-. It will be shown that parts of the [Zn8O13] network are fragments of the ZnO structure showing O2- within a tetrahedral zinc coordination. A deficit of two O2- ions per unit cell is focused on two point positions.
Notizen:
Durch Hochtemperaturreaktionen wurden Einkristalle von Ba2Er2Zn8O13 dargestellt und anschließend röntgenographisch untersucht. Die Verbindung kristallisiert in einem neuen Strukturtyp mit orthorhombischer Symmetrie, Raumgruppe C122v—Cmc21; a = 6,276; b = 10,871; c = 10,195 Å; Z = 2. Die bisher unbekannte Kristallstruktur zeigt Zn2+ in tetraedrischer, Er3+ in oktaedrischer und Ba2+ in kuboktaedrischer Koordination von O2-. Es wird gezeigt, daß das [Zn8O13]-Gerüst Fragmente der ZnO-Struktur mit O2- in tetraedrischer Zinkkoordination enthält. Ein Defizit von zwei O2 pro Elementarzelle verteilt sich auf zwei Punktlagen.
Zusätzliches Material:
3 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/zaac.19946200323