Investigations on the martensitic transformation by sliding friction in relation to contact temperature and wear of soft iron and medium carbon steel (C 45). Using a special experimental procedure, in dependence on sliding velocity and load, martensitic transformations were locally generated on the sliding surfaces (unlubricated) of C 45/C 45 on the contrary to soft iron. Accordingly the coefficient of friction and wear were greatly reduced. This proves the influence of locally high temperatures (flash temperatures). Because of the unknown kinetics of martensitic transformation during rubbing, it is only possible to estimate the temperature. Comparison with calculated flash temperatures shows approximate agreement.
Notes:
Bei Gleitreibungsversuchen C 45/C 45 (ungeschmiert) wurde mit bestimmter Versuchstechnik, abhängig von Geschwindigkeit und Belastung, im Gegensatz zu Weicheisen örtlich Reibmartensit erzeugt. Dadurch starker Abfall von Reibung und Verschleiß. Beweis für die Wirkung hoher örtlicher Temperaturen (Blitztemperaturen). Bei verschieden hohen Beanspruchungen ergeben sich unterschiedliche Verschleißformen. Die nicht bekannte Umwandlungskinetik von Reibmartensit erlaubt von der Werkstoffseite her nur eine Abschätzung der Temperatur. Vergleich mit rechnerisch ermittelten Blitztemperaturen zeigt bei den angewandten Bedingungen annähernd Übereinstimmung.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19720030204