Dissolving-speed of iron in 0,1n-hydrochloric acid1For polished test pieces of iron the increased dissolving-speed in 0,1n-hydrochloric acid in the first seconds is due to the effect of a surface-oxyde.Tests with iron pieces without surface-oxyde (reduction in hydrogen, no touching of the reduced sample with air) show an increasing of the initiating dissolving-speed as well in aqueous as in etheric hydrochloric acid, which may be explained by an increased reactivity of active iron-atoms of the surface. At coarse-field aerated test-pieces the effect of the surface-oxyde is smaller than the increased activity of the surface.The diagram of solubility of polished (surface-oxyde) samples is distinctly different to that field (surface activity) test-piecees.
Notes:
1Bei geschliffenen Eisenproben wird die erhöhte Auflösungsgeschwindigkeit in 0,1n HCl in den ersten Sekunden auf die Wirkung eines Oberflächen-oxydes zurückgeführt.2Versuche mit Eisenproben ohne Oberflächenoxyd (Reduktion in Wasserstoff, keine Berührung der reduzierten Probe mit Luft) zeigen sowohl in wässeriger als auch in ätherischer Salzsäure eine Erhöhung der Anfangs-Lösungs-geschwindigkeit, die durch eine erhöhte Reaktionsfähigkeit aktiver Eisenatome der Oberfläche zu erklären ist. Bei grobgefeilten belüfteten Proben tritt die Wirkung des Oberflächenoxydes gegenüber der erhöhten Aktivität der Oberfläche in den Hintergrund.3Der Charakter der Lösbarkeits-kurven der geschliffenen (Oberflächenoxyd) bzw. gefeilten (Oberflächenaktivität) Proben ist deutlich verschieden.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19510021003