The Oxidation of TitanumIt was attempted to explain the time equations which have been found by different authors. There is a significant connection between the time equations of the different ranges of temperature and times of oxidation. Below 300° C where oxidation follows a logarithmic time equation no solubility of oxygen in titanium during the oxidation could be observed. Above this temperature absorption of oxygen becomes noticeable. In this range of temperature a transition from the logarithmic over a cubic to a parabolic time equation is observed. Above 700° C after longer times of oxidation cracking of the tinder coat must be expected.
Notes:
Es wird der Versuch unternommen, die von den einzelnen Autoren gefundenen Zeitgesetze zu deuten. Die in den verschiedenen Temperaturbereichen und Oxydationszeiten beobachteten Zeitgesetze stehen in einem sinnvollen Zusammenhang. Unterhalb 300° C, wo das logarithmische Zeitgesetz der Oxydation herrscht, ist eine nennenswerte Sauerstofflöslichkeit im Titan während der Oxydation nicht zu beobachten. Erst oberhalb dieser Temperatur wird die Sauerstoffaufnahme durch Titan beachtlich. In diesem Temperaturbereich wird ein Übergang zunächst in das kubische und anschließend in das parabolische Zeitgesetz gefunden. Oberhalb 700° C ist ferner nach längeren Oxydationszeiten mit einem Aufreißen der Zunderschicht zu rechnen.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19560071107