Hydrogen induced stress corrosion cracking at the fusion line between a low-alloy steel and high-alloy weld metalBy analyzing the failure of welded joint consisting of low-alloy steel and high-nickel weld metal, a narrow zone of martensitic structure and high hardness was detected immediately adjacent to the fusion line. Within this region cracks had originated as a result of the simultaneous action of absorbed atomic hydrogen and mechanical stress. A similar situation arises when stainless steel based weld metal is used in welding unalloyed steel. In neither case, heat treatment provides a suitable measure to prevent the kind of failure observed.
Notes:
Bei der Aufklärung eines Schadens wurde erkannt, daß entlang der Schmelzgrenze zwischen einem hochnickelhaltigen Schweißgut und einem niedriglegierten Stahl ein sehr schmaler Saum mit martensitischem Gefüge und hoher Härte vorliegt. Hier war es unter der gleichzeitigen Wirkung von eindiffundiertem atomarem Wasserstoff und einer mechanischen Beanspruchung zu Trennungen gekommen. Dieselbe Gefahr besteht auch am Übergang von unlegiertem Stahl zu einem Schweißgut auf der Basis austenitischer Stähle. Abhilfe durch eine Wärmebehandlung ist nicht möglich.
Additional Material:
12 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19870381007