Particulate-filled thermosetting composites are widely used, yet little systematic work has been done on their long-term strength characteristics. In this study short-term tensile, flexural, and impact tests as well as tensile creep-rupture tests were made for unfilled and filled epoxy to clarify the effects of filler size, filler content, and temperature. Fillers used were silica, alumina particles, and glass beads. Test temperatures were varied from 25 to 110°C. As a result of short-term testing, it was found that the Petch relation held between strength and filler size if brittle fracture occurred, while a strength and filler size if brittle fracture occurred, while a strengthening effect existed when ductile fracture occurred. On creeprupture testing, a strengthening is observed with filler size and content for silica and glass beads. The Arrhenius plot of rupture time for various filler sizes and contents converges to a characteristic point corresponding to the glass transition temperature of the material. Using this relation, a modified Larson-Miller master rupture curve is proposed which can predict the long-term strength of particulate-filled thermosetting composites as functions of rupture time, temperature, filler size, and content.
Additional Material:
13 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pen.760140903