Description / Table of Contents:
Combined with the sudden increase of the susceptibility of antiferromagnetic VO2 at a temperature of about 70°C, the electric conductivity of VO2 is strongly increased, too. Isomorphic substitution of V4+-ions by Ti4+-ions disturbs the antiferromagnetic interaction within the lattice. VO2—TiO2-mixed crystals exhibit higher susceptibilities and conductivities than pure VO2 does; there is a reduced increase of both the susceptibility and conductivity at about 70°C.The spectrum of reflection of VO2 is changed by Ti4+-ions in the same manner like that of pure VO2 when heated above 70°C.
Notes:
Mit dem sprunghaften Anstieg der Susceptibilität von reinem VO2 bei ∼ +70°C ist ein starker Anstieg der elektrischen Leitfähigkeit verbunden. Durch isomorphen Ersatz von V4+ durch Ti1+ werden die antiferromagnetischen Wechselwirkungen im VO2-Gitter gestört. Dies gibt sich an VO2—TiO2-Mischkristallen durch einen Anstieg der Susceptibilität und der Leitfähigkeit sowie durch eine Erniedrigung des Susceptibilitäts- und Leitfähigkeitssprunges in der Gegend von +70°C zu erkennen.Die Farbkurven von VO2 zeigen bei Einbau von Ti4+-Ionen in das VO2-Gitter die gleichen charakteristischen Veränderungen, wie sie bei reinem VO2 oberhalb +70°C auftreten.
Additional Material:
9 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19582970102