Description / Table of Contents:
Preparation, Crystal Structure and Properties of Ag10Si3S11The novel orange-red thiosilicate Ag10Si3S11 is formed besides Ag8SiS6 by the high - temperature reaction between Ag2S, Si and S. The single crystal structure analysis shows the compound to be silver orthothiosilicate thiodisilicate-(1:1) Ag10(SiS4)(Si2S7). The mean Si—S bond lengths are 2.137 Å for SiS4(4-) and 2.129 Å for the hitherto unknown Si2S7(6-). The cation sublattice is slightly imperfect. inferring a certain mobility of the Ag+ ions. Ag10Si3S11 crystallizes in the triclinic space group P1. Lattice constants see „Inhaltsübersicht“.The vibrational spectrum (IR) shows absorptions within the characteristic spectral regions for asymmetric and symmetric stretching vibrations of the SiS4 tetrahedra at 490-515 and 423-433 cm-1.
Notes:
Neben Ag8SiS6 entsteht bei der Hochtemperaturreaktion von Ag2S mit Si und S das bisher unbekannte orangerote Ag10Si3S11. Die Einkristall-Röntgenstrukturanalyse zeigt, daß die Substanz als Silber-orthothiosilicat-thiodisilicat-(1:1) Ag10(SiS4)(Si2S7) zu formulieren ist. Die mittleren Si—S-Bindungslängen betragen 2,137 Å im SiS4(4-), 2,129 Å im bisher noch nicht beobachteten Si2S7(6-). Das Kationenteilgitter ist leicht gestört und deutet auf eine gewisse Beweglichkeit der Ag+-Ionen im Kristall hin. Ag10Si3S11 kristallisiert triklin (P1) mit a = 12,414, b = 13,476, c = 6,459 Å, α = 78,92°, β = 77,61°, γ = 68,71°, Z = 2.Das Schwingungsspektrum (IR) zeigt Absorptionen in den für asymmetrische und symmetrische Valenzschwingungen der SiS4-Tetraeder charakteristischen Bereichen bei 490-515 bzw. 423-433 cm-1.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19764200104