Lithium nitride hydride
;
crystal structure
;
Chemistry
;
Inorganic Chemistry
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
Description / Table of Contents:
Preparation and Crystal Structure of Lithium Nitride Hydride, Li4NH, Li4NDSingle phase Li4NH was prepared by the reaction of Li3N and LiH at 490°C. Its structure has been solved from x-ray and time-of-flight neutron powder diffraction data.Li4NH crystallizes in an ordered variant of the Li2O structure. N and H occupy the sites of two interpenetrating “extended” diamond lattices. Li occupies all N2H2 tetrahedral voids and is found to be shifted into a N2H tetrahedral face. As a result H is in compressed tetrahedral coordination by Li, while N is in bisdisphenoidal coordination by Li. Alternatively, the Li4NH structure may be regarded as a [Li4N]+threedimensional net, its voids being filled up with H-.Li4NH is a reactive solid, which decomposes to imide when in contact with N2 or H2 at some 400°C.
Notes:
Li4NH wurde durch Reaktion von Li3N und LiH bei 490°C erhalten. Die vollständige Strukturbestimmung gelang über Röntgen- und Flugzeit-Neutronen-Pulverdiffraktion.Li4NH kristallisiert in einer Ordnungsvariante der Li2O-Struktur (Raumgruppe I41/a, a = 489.18(1), c = 993.21(3) pm, Z = 4). N und H besetzen die Plätze von zwei ineinander gestellten gestreckten Diamantgittern. Li besetzt, in Richtung einer N2H-Dreiecksfläche ausgelenkt, alle N2H2-Tetraederlücken. Als Folge ist H gestaucht tetraedrisch und N verzerrt kubisch von Li koordiniert. Alternativ läßt slch die Struktur der Titelverbindung als ein [Li4N]+-Raumnetz deuten, in dessen Hohlräume zum Ladungsausgleich Hydridionen eingebaut sind.Li4NH reagiert bei höheren Temperaturen mit N2 bzw. H2 unter Imidbildung.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19976231215