Synthesis and Structure of Li2Ta2O3F6Colourless crystals of Li2Ta2O3F6 are obtained by heating a mixture of LiTaF6 and LiTaO3 in a sealed nickel tube to 700°C for 5 days, followed by slow cooling to room temperature. Li2Ta2O3F6 is also a product of controlled hydrolysis of LiTaF6. It crystallizes in the trigonal space group P3121 with a = 558.11(3), c = 2096.10(4) pm, and Z = 3. The structure is built up by corner-sharing TaO3F3-octahedra forming anionic double layers parallel (001). The lithium cations are intercalated between these double layers having a square-pyramidal coordination by fluorine atoms. For the educt LiTaF6 a new high-temperature modification was found, which is reversibly formed at 150°C. It crystallizes with a = 783.5 pm in the cubic NaSbF6 type.
Notes:
Farblose Kristalle von Li2Ta2O3F6 entstehen beim längeren Erhitzen eines Gemenges aus LiTaF6 und LiTaO3 in einer Nickelampulle auf 700°C und anschließendem langsamen Abkühlen. Li2Ta2O3F6 bildet sich außerdem bei der kontrollierten Hydrolyse von LiTaF6. Es kristallisiert trigonal in der Raumgruppe P3121 mit a = 558,11(3); c = 2096,10(4) pm und Z = 3. In der Verbindung sind TaO3F3-Oktaeder über Ecken zu anionischen Doppelschichten parallel (001) verknüpft. Die Lithiumionen sind zwischen den Doppelschichten eingebaut und tetragonal-pyramidal durch Fluoratome koordiniert. Für das Edukt LiTaF6 wurde eine neue Hochtemperaturphase gefunden, die sich bei 150°C reversibel bildet und im kubischen NaSbF6-Typ mit a = 783,5 pm kristallisiert.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19976230173