The Henry's law and diffusion constants of vinyl chloride in poly(vinyl chloride) were determined at temperatures of 24, 90, 120, 150, and 170°C for weight fractions of vinyl chloride between 0.2 × 10-3 and 0.8 × 10-3. Above 90°C, Henry's law applies; values of the constant increase with temperature from 1.8 × 102 to 5.5 × 102 atm per unit weight fraction of dissolved vinyl chloride. The heat of desorption is about 15 kJ/mole. At 24°C, the nominal Henry's law constant was smaller than would have been obtained by extrapolating the values found at higher temperature. The diffusion constants increase with temperature from about 2 × 10-13 to 3 × 10-7 cm2/sec. The activation energy for diffusion is about 110 kJ/mole between 90 and 170°C. Although all values were determined in the absence of air, it is likely that they apply to polymer in air. They may, therefore, be used to calculate the vinyl chloride content in the gas above poly(vinyl chloride) under specific processing conditions.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1977.170151108