The weight-average molecular weights of polymers of acrylonitrile prepared by a free-radical initiator and an organometallic catalyst have been determined by lightscattering measurements in N,N-dimethylformamide, dimethyl sulfoxide, and dimethylacetamide at 25°C. and in dimethyl sulfoxide at 140°C. The apparent molecular weights of the polymers prepared with the NaAlEt3S(i-Pr) catalyst in DMF at -78°C. (referred to as high-melting polymers) changed from 54,800, 82,700, and 480,000 when measured in DMF at 25°C. to 36,000, 41,600, and 225,000 when measured in DMSO at 140°C., whereas the molecular weights of the free-radical polymers remained unchanged. Furthermore, from results obtained in DMSO at 140°C., The intrinsic viscosity-molecular-weight relationships were found to be identical for the high-melting and the free-radical polymer and in substantial agreement with an equation reported by Cleland and Stockmayer. The apparent decrease in molecular weight of the high-melting polymer from 25 to 140°C. indicates rather clearly that the high-melting polymers are associated in DMF at 25°C. The “aggregates,” even though present only at low concentrations, raised the weight-average molecular weight markedly but affected the number-average molecular weight only slightly, thus giving a high M̄w/M̄n ratio. It appears likely that when temperature and solvent are such that association does not occur, linear PAN's will have approximately the same intrinsic viscosity-molecular weight relationship (subject of course to slight change by polydispersity). The often reported abnormal molecular weight of samples prepared by solution polymerization especially at low temperatures, may be attributed to branching, or to an association, as reported here. The nature of association of PAN in dilute solution is also discussed.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1967.160050109