Polyacrylonitrile crystals were grown from dilute solutions of propylene carbonate by a technique similar to that described by Holland et al. Crystals were also grown on various substrates and sampled at various stages of growth after washing away the uncrystallized solution. The initial single lamellae rapidly develop into complex twinned structures with many overgrowths. The morphology of the full-grown crystal varied considerably with crystallization temperature. Small-angle x-ray and electron microscopy results indicate only a small change in lamellar thickness with crystallization temperature for our polymer. Electron and x-ray diffraction results indicate lateral order can be quite good in these crystals. Our x-ray results indicate that the previously reported a and b parameters should be doubled to give a = 21.18 Å and b = 11.60 Å. However, there was no evidence for chain-axis order. The crystals were stretched at various stages of growth on Mylar film. Multilamellar crystals having their long axis parallel to the draw direction formed large cracks perpendicular to the long axis. Fibers of large diameter (100-250 Å) were observed across these cracks. When the long axis of these crystals was at an angle to the draw direction no large cracks or fibers were observed. Single lamellae generally cracked perpendicular to the draw direction, irrespective of their orientation to the draw direction. Definite fibers were not observable across cracks in single lamellae.
Additional Material:
17 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1968.160060714