ISSN:
0887-6266
Keywords:
poly(cis-benzoxazole)
;
poly(trans-benzothiazole)
;
lyotropic
;
liquid crystalline
;
monofilament
;
x-ray scattering
;
compressive strength
;
Chemistry
;
Polymer and Materials Science
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
,
Physics
Notes:
The results of a series of novel synchrontron-based in situ x-ray scattering experiments of monofilament fiber drawing from lyotropic solutions of poly(cis-benzoxazole) (PBO) and poly(trans-benzothiazole) (PBZT) are reported. The purpose of the study is to determine orientation and microstructure development in the draw zone as a function of shear rate in the capillary die, and spin draw ratio (SDR). The transition of the extrudate from opaque to the transparent is complete at about a SDR = 3 and f of 0.9. The filament orientation parameter (f) was found to depend strongly on spin draw ratio, but not shear rate. The orientation was found to increase down the extrudate toward completion of the draw down as one proceeds further from the die face up to an extrudate length of 3.8 cm. Coherence lengths on the order of 19 nm (axial), and 4.5 nm (lateral) have been observed. These “microdomain” sizes are consistent with the “crystallite” sizes typically observed in coagulated fiber. The occurrence of these microdomains in the draw zone as a precursor to the microfibrillar structure is believed to be the origin of low filament compressive strength. © 1994 John Wiley & Sons, Inc.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/polb.1994.090321602