A series of polysiloxane-block-polyimides were synthesized by solution imidization of the polyamic acids derived from the combination of 3,3′,4,4′-diphenylsulfonetetracarboxylic dianhydride (DSDA), 2,2-bis[4-(4-aminophenoxy)phenyl]propane (BAPP), and diamino(polysiloxane) (PSX (Mw = 750)) in N-methyl-2-pyrrolidone (NMP). Their structures were analyzed by 1H-, 13C-, and 29Si-NMR spectra as well as by IR spectroscopy. The solid-state NMR spectrum was also measured to determine the spin-lattice relaxation time of the copolyimides. The observed relaxation times of both aromatic and polysiloxane segments were similar in the copolyimides having 10-30 wt % of PSX, while those in the copolyimide with 50 wt % of PSX was significantly different. This may be attributed to the morphology change due to the increase in PSX composition in the polymer backbone. The reduced viscosity of the copolyimides could be controlled by changing the monomer ratio in the feed or by adding an end-capping reagent such as phthalic anhydride into the polymerization system. The kinetic study of the solution imidization revealed that the imidization reaction obeyed second-order kinetics. The activation energy calculated for this imidization was 99.2 kJ/mol, being similar to that for the imidization of the DSDA-based aromatic polyimides. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2237-2245, 1998
Additional Material:
10 Ill.
Type of Medium:
Electronic Resource