acoustic emission measurements
;
compression testing
;
nickel oxide
;
oxide-scale failure
;
pseudoplasticity
;
TEM
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract Stresses formed in oxide scales due to oxide growth are usually of a compressive nature, and there is still some debate on how these stresses are accommodated. While the deformation behavior of oxide scales under tensile stresses can be regarded as fairly well understood, there are many open questions concerning scale deformation and cracking under compressive straining. Therefore, the NiO scale formed on two different grades of Ni was chosen as a model system for compression tests with strain rates ranging from 8×10−4 to 8×10−8 s−1 in the temperature range of 20 to 800°C. Test environments were air and argon, and accompanying acoustic-emission measurements were taken in order to detect the beginning of oxide-scale cracking during straining. As a result the critical-strain values at the beginning of mechanical-scale damage could be determined quantitatively and explained consistently by model considerations. Furthermore, SEM and TEM investigations, backed up by sulfur decoration of microcracks at the end of the tests, revealed that at elevated temperatures a major deformation mechanism under these conditions takes the form of dynamic equilibrium of continuous microcracking with superimposed oxide-healing processes, making compressive strains of 10% and more possible without macroscopic scale failure. It is, therefore, assumed that a major mechanism of growth stress relief in oxide scales occurs via microcracking and scalecrack healing.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01061927