Journal of Applied Physics
74 (1993), S. 754-756
ISSN:
1089-7550
Source:
AIP Digital Archive
Topics:
Physics
Notes:
A shallow Pd/Ge/Ti/Pt/ohmic contact for both n- and p-GaAs has been investigated. The contacts were rapid thermally annealed in N2 for 15 s at temperatures from 350 to 550 °C. The lowest average specific contact resistances were 4.7×10−7 and 6.4×10−7 Ω cm2 for the n- and p-GaAs, respectively, when the n-GaAs was doped with Si to 2×1018 cm−3 and the p-GaAs was doped with carbon to 5×1019 cm−3. Electrical measurements and Auger depth profiles showed that the contacts were stable as they remained ohmic after an anneal at 300 °C for 20 h for both n- and p-GaAs. The p contact is more stable than the n contact at the higher temperatures where there is more As outdiffusion as determined by Auger depth profiles. Transmission electron microscopy showed that the interfaces between the p-GaAs and the contacts were smooth for both as-grown and annealed samples, and no oxides were detected.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.355248
Library |
Location |
Call Number |
Volume/Issue/Year |
Availability |