Several Fe – O samples containing different fractions of dispersed oxides were processed by mechanical milling followed by consolidating rolling. The samples were annealed at 1000oC and then compressed to strains of 0.35, 1.2, and 1.9 at an ambient temperature. Dispersed oxides with size of about 20 nm were homogeneously distributed throughout the ferrite matrix and their volumefractions varied from about 0.3% to 2.0%. To study the annealing softening mechanisms, the coldworked specimens were annealed for an hour at 700oC and 800oC. The fine dispersion of oxide particles was very effective to suppress any softening processes. Primary recrystallization fully developed in the samples with volume fraction of dispersed oxides of about 0.3%. Increase in the fraction of dispersed oxides resulted in decrease of the fraction recrystallized. In the samplescontaining 2.0 vol.% of dispersed oxides, only recovery was the annealing softening process irrespective of the preceding cold strain. The critical volume fraction of dispersed particles for development of the primary recrystallization is considered to range from 0.5 to 2.0%
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.467-470.229.pdf