Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
The hot deformation behavior of a low carbon Nb-microalloyed steel is investigated by hot compression test in the ferrite phase region compared with a low carbon steel with similar compositions, and the effect of Nb on dynamic recrystallization of ferrite is analyzed. Results indicate that during hot deformation in the ferrite phase region, the effect of Nb solely depends on the size of NbC precipitates. Tiny particles which average size is about 7.5nm have a retarding effect on dynamic recrystallization process of ferrite, on the contrary, coarser particles which average size is about 30.6nm have a promoting effect and are of benefit to the refinement of recrystallized grains
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.475-479.149.pdf