Barium strontium titanate (Ba0.8Sr0.2TiO3) thin films have been prepared on Pt/Ti/SiO2/Si substrates using a soft solution processing. X-ray diffraction and also micro-Raman spectroscopy showed that the Ba0.8Sr0.2TiO3 thin films exhibited a tetragonal structure at room temperature. The presence of Raman active modes was clearly shown at the 299 and 725 cm−1 peaks. The tetragonal-to-cubic phase transition in the Ba0.8Sr0.2TiO3 thin films is broadened, and suppressed at about 35 °C, with a maximum dielectric constant of 948 (100 kHz). Electrical measurements for the prepared Ba0.8Sr0.2TiO3 thin films showed a remnant polarization (Pr) of 6.5 μC/cm2, a coercive field (Ec) of 41 kV/cm, and good insulating properties. The dispersion of the refractive index is interpreted in terms of a single electronic oscillator at 6.97 eV. The direct band gap energy (Eg) and the refractive index (n) are estimated to be 3.3 eV and n = 2.27–2.10, respectively. © 2002 American Institute of Physics.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1063/1.1466526
| Bibliothek |
Standort |
Signatur |
Band/Heft/Jahr |
Verfügbarkeit |