Keywords:
dynamic response
;
Epon 828
;
T-403
;
epoxy
;
high-strain rate test
;
Hopkinson bar
;
material modeling
;
strain-rate effects
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract The uniaxial compressive mechanical response of an epoxy, Epon 828/T-403, was experimentally, measured over a strain-rate range of 1.1 × 10-4 to 5.2 × 103 s-1. A modified split Hopkinson pressure bar was employed to apply dynamic compressive loading over a very short time of ∼ 0.2 millisecond, whereas an MTS was used to conduct quasi-static experiments at a duration of 0.2 to 2,000 seconds to determine strain-rate sensitivity. The experimental results show that the compressive strength of the epoxy increases with increasing strain rate until adiabatic heating offsets the strain-rate hardening. A constitutive model based on the Johnson–Cook model was constructed to describe the stress-strain behavior of the epoxy at the strain rates tested. A Ludwig equation was modified to model the stress-strain behavior at a reference strain rate, which included elastic deformation, a yield-like peak, and a strain-softening region. A hyperbolic tangent function provided a good description of the strain-rate effect. The material constants in this proposed model were determined using the experimental results.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1023/A:1009866108965
Permalink