ISSN:
1573-4889
Keywords:
oxidation
;
hot corrosion
;
nickel alloys
;
composites
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract The oxidation and hot corrosion behavior of a tungsten-fiber, reinforced Ni~ 20Cr alloy has been examined under the following exposure conditions: (a) pure oxygen at 1 atm pressure; (b) sulfidation in H2–10 %H2S; (c) presulfidation in H2–10 %H2S followed by oxidation in oxygen; and (d) oxidation in 1 atm oxygen after precoating with approximately 1 mg/cm2 of Na2SO4. Rapid oxidation of the tungsten fibers causes considerable distortion of the matrix and catastrophic degradation of the matrix follows. Inter diffusion between the matrix and the fibers is also important. During sulfidation, only the matrix forms sulfides, the fibers remaining unaffected. Consequently, presulfidation, although having a dramatic effect on the oxidation of the matrix does not have a damaging effect on the fibres. Equally, the presence of sodium sulfate is not critical, although severe oxidation of the exposed tungsten fibers is still observed.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00613494
Permalink