Abstract The YBCO/Ag superconducting composites were fabricated by compressing powders of YBCO and silver mixed at various volume proportions 0 to 100% under pressures of 2.0 and 5.4 GPa and subsequently sintering at 900 °C for 10 h in a flowing oxygen atmosphere. The superconducting transition temperature, particularlyT c (R=0), was found to retain the value above 85 K up to 50 vol % Ag while the normal resistivity at 300 K to reduce below 10 μΩcm. The highestJ c of 400 Acm−2 was attained for the sample containing 20 vol % Ag pressed at 5.4 GPa. The mechanical properties were also improved by the addition of silver: the compressive strength is increased by two to three times and the maximum strain, which is a measure of ductility, reached a value almost four times as large as that in the pure YBCO prepared under the ordinary pressure of 0.5 GPa. The persistence of the superconducting characteristics up to 70 vol % Ag is discussed in terms of the microstructure taken with the scanning electron microscope.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00588312
Permalink