Pitting corrosion under hydrogen bubbles, adherent to the surface of zincInvestigation zinc alloys in acid solutions, it could be determined that under hydrogen bubbles which has adhered on the surface, annuker pitting corrosion took place. The types of corrosion attack were examined under a microscope during and after the corrosion test and in some cases under scanning electron microscope. The formation of the annular pittings can be interpreted as an impoverishment of hydrogen ions in the boundary layer between the hydrogen bubble and the surface of the specimen.
Notes:
Bei Korrosionsuntersuchungen an Zinklegierungen im sauren Korrosionsmedium konnte festgestellt werden, daß an Stellen anhaftender Wasserstoffblasen auf der Probenoberfläche ringförmiger Lochfraß entsteht. Diese Korrosionserscheinungen wurden während und nach dem Korrosionsversuch mit dem Lichtmikroskop und dem Rasterelektronenmikroskop untersucht. Das Entstehen dieser ringförmigen Lochfraßnarben kann durch die Verarmung von Wasserstoffionen in der Grenzschicht zwischen Wasserstoffblase und Probenoberfläche erklärt werden.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19710220407
Permalink