Description / Table of Contents:
Mechanical working of Ni crystals leads to surface deformations being typical for c. f. c. lattices. By interaction with H2S (formation of NiS), a chemical decoration of the gliding strips is possible which allows, by means of normal and electron microscope techniques, to study the mechanochemically activated surface areas of single- and polycrystalline Ni. Annealing after the mechanical working results first in a decrease of the chemical activity and then, at sufficiently high temperatures, in a complete loss of activity and chemical decoration.
Notes:
Bei der mechanischen Bearbeitung von Ni-Kristallen entstehen auf der Oberfläche die für kubisch-flächenzentrierte Kristalle typischen Deformationsstrukturen. Ausgehend von den Vorstellungen über erleichterte Keimbildungsbedingungen in Bereichen hoher Spannungskonzentration, in denen hohe Versetzungsdichten auftreten, lassen sich die entstehenden Gleitbänder durch H2S-Einwirkung unter Bildung von Nickelsulfid auf chemischem Wege dekorieren. Unter Anwendung mikroskopischer und elektronenmikroskopischer Methoden werden mit diesem Verfahren die bei der mechanischen Beanspruchung von Einkristallen und Polykristallen auftretenden Störbereiche nachgewiesen. Die Temperung der Kristalle nach Abschluß der mechanischen Bearbeitung führt zu einer Abnahme der Aktivität. Bei genügend hohen Temperaturen geht schließlich die selektive Reaktion an Gleitbändern vollständig verloren und führt zu einem Verlust des Dekorationseffektes.
Additional Material:
16 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19653380115
Permalink