On the corrosion of binary CuAl alloys in sulfuric acidThe corrosion of binary CuAl-Alloys with Al-concentrations up to 16.5 w/o was investigated after different heat treatments in 1N sulfuric acid at 25°C. The corrosion behaviour of the various phases was characterized by potentiodynamic polarization curves and by long term potentiostatic tests combined with metallographic investigations of corroded electrodes. Within a limited potential range the results confirm the excellent corrosion resistance of the α-phase and the effect of dealuminization of all other phases. The origin of these differences in corrosion behaviour is discussed.
Notes:
Bei 25°C wurde in 1N Schwefelsäure die Korrosion binärer Al-Legierungen mit Al-Konzentrationen bis zu 16,5 Gew. % und unterschiedlicher Wärmebehandlung untersucht. Das Korrosionsverhalten der einzelnen Phasen wurde durch potentiokinetische Stromspannungskurven und durch potentiostatische Dauerpolarisationsversuche charakterisiert, die durch metallographische Untersuchungen an korrodierten Elektroden ergänzt wurden. Innerhalb eines begrenzten Potentialbereichs wurde die ausgezeichnete Korrosionsbeständigkeit der α-Phase und das Auftreten von Entaluminierung in allen übrigen Phasen bestätigt. Die Ursachen für diese Unterschiede im Korrosionsverhalten werden diskutiert.
Additional Material:
12 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19780290606
Permalink