Texture formation through strain induced boundary migration (SIBM) was investigated. Temper rolling reduction before final annealing for SIBM was varied between 0 and 26% and grain sizes and textures were measured using EBSD. In the specimen which was temper rolled to 5%, in which grain growth by SIBM occurred most efficiently, a strong Goss component (which was a minorcomponent after rolling), developed during annealing. From the EBSD image quality analysis, it was found that stored energy increased significantly in the Goss component with strain (from 5 to 9 %), whereas it was always relatively small in the D-Cube component ({001}〈110〉), compared to Goss and g-fibre components. Based on these results, a mechanism of grain growth by SIBM wassuggested. Texture evolution during annealing could thus be explained by the hypothesis, speculated from the analysis of orientation stability, that D-Cube grains are associated with more homogeneous dislocations distributions than Goss grains, in which the co-existence of high and low dislocation density zones could favour grain growth by SIBM
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.467-470.893.pdf
Permalink