The Response of Alloys to Erosion-Corrosion at High Temperatures (1998)

Link, R. J. ; Birks, N. ; Pettit, F. S. ; [weitere]

Springer

Oxidation of metals 49 (1998), S. 213-236

zur Merkliste hinzufügen auf der Merkliste

Details

ISSN: 1573-4889

Schlagwort(e): OXIDATION ; EROSION ; EROSION-CORROSION ; Ni-Cr ALLOYS

Quelle: Springer Online Journal Archives 1860-2000

Thema: Maschinenbau

Notizen: Abstract Pure nickel, Ni-20Cr and Ni-30Cr alloys wereexposed to conditions of erosion and corrosionsimultaneously at 700°C and 800°C. The exposureswere made using normal impact of an air stream loadedwith 20-μm alumina. The alumina particles flowed at therate of 400 mg per min and the velocities used were 75m/s and 125 m/s. The reaction kinetics were measureddiscontinuously by interrupting the exposure and measuring the weight loss. The specimens wereexamined using SEM-EDAX both on the surface and incross-section. Under simple oxidation, the alloyspecimens developed a thin protective layer of chromia. Under erosion-corrosion conditions, thisprotective scale was prevented from forming and thealloys were found to undergo aggressive attack at a ratethat was the same as that experienced for pure nickel, the surface oxides were identified asCr2O3 and NiO. It is proposedthat, under erosion corrosion, the erosive streamprevents the formation of a continuous layer of chromiaby removing the oxide faster than it can spread laterally. The specimen issaid to be in a state of erosion-maintained transientoxidation. This mechanism implies that it would bedifficult for protective scales to form in the presence of erosion and the oxidation behavior of analloy cannot be used as a guide to its resistance toerosion-corrosion.

Materialart: Digitale Medien

URL: http://dx.doi.org/10.1023/A:1018886509459

Permalink

Bibliothek	Standort	Signatur	Band/Heft/Jahr	Verfügbarkeit

Andere fanden auch interessant ...

Artikel (Nationallizenzen)

Volltext

Digitale Medien

Die Reaktion von Borsäuremethylester mit Ammoniak und Aminen. III (1952)

Goubeau, J. ; Link, R.

Weinheim : Wiley-Blackwell

Zeitschrift für anorganische Chemie 267 (1952), S. 27-36

zur Merkliste hinzufügen auf der Merkliste

Details

ISSN: 0044-2313

Schlagwort(e): Chemistry ; Inorganic Chemistry

Quelle: Wiley InterScience Backfile Collection 1832-2000

Thema: Chemie und Pharmazie

Notizen: Durch Reaktion von Borsäuremethylester mit Methyl-, Dimethyl- und Trimethylamin werden die entsprechenden Anlagerungsprodukte B(OCH3)3 · NHx(CH3)3-x (x = 2,1,0) dargestellt, einige physikalische Daten dieser Substanzen bestimmt und vom Dimethylamin-Anlagerungsprodukt ein tensimetrischer Abbau durchgeführt, der zu einem definierten Zwischenprodukt führt,

Zusätzliches Material: 2 Ill.