Microstructure and Corrosion Behaviour of a Nitrogen Alloyed Stainless SteelThe corrosion behaviour of a nitrogen alloyed stainless steel is investigated using potentiodynamic anodic polarization in physiological NaCl solution. The microstructure of forged samples is determined by microscopy and hardness measurements. The steel shows a globular austenitic structure. In the zone of large forging deformation the grains are elongated. Precipitates are observed in which chromium and molybdenium are enriched. The breakdown potentials range from 200 to 1170 mV vs. SCE, most of the values exceed 500 mV. The breakdown potentials decrease with increasing aspect ratio of the grains and increasing hardness. The precipitates are initial sites for pitting and crater shaped metal dissolution.
Notes:
Das Korrosionsverhalten eines stickstofflegierten rostfreien Stahles wird durch potentiodynamische anodische Polarisation in physiologischer NaCl-Lösung untersucht. Der Gefügezustand geschmiedeter Proben wird mikroskopisch und durch Härtemessungen ermittelt. Der Stahl weist ein globulares austenitisches Gefüge auf, in der Zone starker Schmiedeverformung sind die Körner gestreckt. Es liegen Ausscheidungen vor, in denen Chrom und Molybdän angereichert sind. Der Stahl zeigt Durchbruchspotentiale zwischen 200 und 1170 mV vs. SCE, die meisten Werte liegen über 500 mV. Die Durchbruchspotentiale fallen mit zunehmendem Streckungsgrad der Körner und zunehmender Härte ab. Die Ausscheidungen sind Initialpunkte für loch- und kraterförmigen Materialabtrag.
Additional Material:
16 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19980290704
Permalink