high-temperature oxidation
;
Fe–Cr–Al alloys
;
cyclic oxidation
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Maschinenbau
Notizen:
Abstract The detailed oxidation behavior of Fe–10Cr alloys, containing aluminumin the range of 2–8% by weight, was studied in pure oxygen at 1 atmpressure. The investigations were performed over the temperature range950–1050°C under cyclic conditions (3-hr cycles) in each case. Thecyclic-oxidation resistance, as measured by the specific weight-gain values,was observed to progressively improve with increasing aluminum content inthe alloy. For a particular aluminum content, however, the oxidationresistance decreased with increasing temperature. Following the initialtransient-oxidation period, a healing layer of chromia was established onthe four alloys. The lower-aluminum alloys (2–4% Al) were observedto end up with Fe-rich oxide scales under the experimental conditions atall temperatures, whereas those containing aluminum in the range of6–8% formed α-Al2O3 scales.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1023/A:1004682316408
Permalink