Preparation and Structure of Niobium Tungsten Oxides (Nb,W)17O47 with Mixed ValencyThe formal substitution of 2Nb5+ by Nb4+ or W4+, respectively, and W6+ leads to tungsten niobium oxides (Nb,W)17O47 with mixed valency. The phases Nb8-nW9+nO47 with n = 1 to 5 could be obtained by heating (1 250°) mixtures of NbO2 or WO2, respectively, with Nb2O5 and WO3. The products crystallize with the structure of Nb8W9O47. This is proved by X-ray powder diffraction and transmission electron microscopy. A further decrease of the Nb-content results in two-phase products.
Notes:
Durch formale Substitution von je zwei Nb5+ durch Nb4+ (bzw. W4+) und W6+ sind - ausgehend von Nb8W9O47 - gemischtvalente Niob-Wolframoxide unterschiedlicher Nb/W-Verhältnisse denkbar, von denen Zusammensetzungen Nb8-nW9+nO47 mit n = 1 bis 5 durch isothermes Erhitzen (1 250°C) der entsprechenden Gemenge von NbO2 (bzw. WO2) mit Nb2O5 und WO3 phasenrein dargestellt werden konnten. Diese Produkte kristallisieren alle in der Struktur des Nb8W9O47 und sind somit als Mischphase (0 ≤ n ≤ 5) aufzufassen, wie die röntgenographische (Pulvermethode) und durchstrahlungs-elektronenmikroskopische Untersuchung belegt. Präparate mit niedrigerem Nb-Gehalt (n 〉 5) erhielten wir dagegen nicht mehr phasenrein.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19956210517
Permalink